Preparation of the Thermoplastic Starch/Montmorillonite Nanocomposites by Melt-intercalation

In this paper, the conception of melt-intercalation was introduced into the natural polymer field, and the thermoplastic starch/ethanolamine-activated montmorillonite (TPS/EMMT)nanocomposites were prepared by extruding the composites of EMMT and TPS, plasticized with ethanolamine/formamide. Wide angle X-ray diffraction (WAXD) and transmission electron microscope (TEM) revealed that TPS was intercalated into the layers of EMMT successfully and formed the intercalation nanocomposites with EMMT. When EMMT content was wt. 10%, the mechanical testing indicated that the tensile stress of the nanocomposites reached 9.69 MPa, and the tensile strain reached 74.07%, Youngs modulus increased from the 47.23 MPa of TPS to 184.11after they had been stored at RH25% for 14 days.

作 者： Ming Fu HUANG Jiu Gao YU Xiao Fei MA   作者單位： School of Science, Tianjin University, Tianjin 300072  刊 名： 中國化學快報（英文版）  ISTIC SCI 英文刊名： CHINESE CHEMICAL LETTERS  年，卷(期)： 2005 16(4)  分類號：   關鍵詞： Thermoplastic starch   montmorillonite   nanocomposites   ethanolamine  

【Preparation of the Thermoplastic Sta】相關文章：

Preparation of TiO2-activated carbon complex membranes and their photoelectrocatalytic activity04-27

Preparation and Characterization of Refuse Derived Fuel for Pyrolysis and Gasification by Bindless High Pressure Briquet04-26

Assessment on the pollution of nitrogen and phosphorus of Beijing surface water based on GIS system and multivariate sta04-25

Preparation and characterization of mixed hydroxy-Fe-Al pillared montmorillonite with large basal spacing04-26

Preparation and mechanism of Fe3O4/Au core/shell super-paramagnetic microspheres04-26